LaSeal 966 High Elastic Low Modulus MS Polymer Sealant
Main purposes
1.For sealing doors and windows;
2.Interior and outdoor using, Weatherproof ;
Characteristics
1.Outstanding anti-mildew property.
2. Excellent mechanical property: 20 class low modulus, long lasting anti-mildew ability.
3.Excellent adhesion to most decoration materials.
4.Good anti-aging and weatherproof ability.
5.Environment friendly, ultra low VOC, odor free.
6.Can be painted over with most surface coatings (compatibility tests recommended)
7.Solvent free, isocyanate and silicone free.
Application
1.Jointing filling and sealing of all kinds of marble, granite curtain wall engineering and cement prefabrication engineering;
2.Concrete expansion joint sealing of road engineering;
3.Sealing of prefabricated building joints and high building expansion joints
4.Sealing of window & door frames, Panel seams and ceilings, Water pipes, roof gutters,movable houses and containers
Technical Data Sheet(TDS)
Technology data:The following data are only for reference purpose, not intended for use in preparing specification
LaSeal 966 High Elastic Low Modulus MS Polymer Sealant
Standard:
Meets or exceeds the requirements of the following specifications:
The requirements of VOC content specifications in LEED credit EQc4.1
“Low-emitting products” of SCAQMD rule 1168.
The French VOC requirements for class A+
CE marked for EN 15651 for façade applications.
Item | Data |
Chemical Base | MS Polymer Based |
Curing Mechanism | Moisture Curing |
Color | White/Black/Grey |
Density | 1.4±0.1 gr/ml |
Tack Free Time ≤ 1h | 10-20 min (23°C and %50 R.H.) |
Cured depth (24hours) | ＞3.5mm (23°Cand %50 R.H.) |
Cured depth (24hours) | ＞3.5mm |
Tensile Strength | ≥1.2MPa |
Elongation at break | ≥500% |
Shear stress | 2.5MPa |
Tear propagation | 15 N/mm |
100% Tensile Modulus | ≥0.4MPa |
Shore A Hardness | 25-35A |
UV resistant | Excellent |
Press Ratio | ＞350ml/min |
Your company | ≤ 1.5% |
Service Temperature | +5°C to +35°C |
Application Temperature | -50℃~120℃ |
Shelf life | 12 months |
Curing condition of the sample :23℃×50%RH×14 days | |
Limitations
● Avoid operating below +5 °C and above +35 °C.
● Do not apply on curing silicones.
● Minimum depth for working joint is 6 mm.
● Maximum expansion and contraction should not exceed 25% of average joint width.
Surface Preparation
● Following cleaning procedure and materials are recommended:
● Glass Degrease with alcohol or MEK
● Aluminium, light alloys and stainless steel Degrease with alcohol or MEK
● Other Metals Lightly abrade then degrease as above
● Wood Lightly abrade surface then remove dust
● Plastics Degrease using an agent recommended by plastics manufacturer
● Concrete and other alkaline Surfaces Brush and remove dust
Instruction
1. Before the application, the tip of the cartridges is cut and a plastic cap is fixed.
2.The tip of the cap is cut according to the width of the surface and fixed to the cartridge gun.
3.The sausage package is cut from one edge and fixed to a suitable gun. Then the cap nut is screwed to the cylinder of the gun.
4.The joints should be filled at one time and without gaps during the application.
5.The surface of LaSeal Universal applied in the joints should be smooth ended with a dampened spatula, glazing tool, joint iron or by hand immediately.
6. If used, the adhesive tape should be removed afterwards.
7.The opened packages should be consumed as quickly as possible.
8.The contaminated areas and used tools should be cleaned with white spirit or alcohol. It is cleaned only mechanically after cured.
9.Joint width/depth ratio should be 2:1.
Storage and shelf life
1.They should be protected from water, frost and adverse air conditions.
2.They should be kept dry and cool on wooden pallets at between +5 degree C and +25 degree C in moisture free conditions.
3.The opened products should be consumed immediately.
4.Shelf life is maximum 12 months conditional to complying with the aforementioned storage conditions.
Technical Data Sheet(TDS)
Technology data:The following data are only for reference purpose, not intended for use in preparing specification
LaSeal 731 Middle Quality Acetoxy Silicone Sealant
Item | Data |
Type | Acetoxy |
Density (g/cm3) | 0.98 |
Capacity movement | ±30% |
skinning time | 5-15 minutes |
Drying time(2mm/h) | 8-10 |
Drying(4mm/h) | 18-22 |
Max. Tensile strength | 1.3 |
Hardness shore A | 21 Judges 2 |
Elongation at Break(%) | =500 |
Modulus Mpa(100%) | 0.60 |
Application temperature | -20 C to +40 C |
Temperature resistance | -50 C to +100 C |
Adhesive | OK |
weatherproof | OK |
Cold-hot adhesive | OK |
under water adhesive | OK |
Elastical Recovery (%) | 96 |
Mass-loss Rate (%) | 35 |
Limitations：The product is not applicable to structure assembly or project whose base material has a surface temperature above 40 ℃.